Composition containing rotigotine and use thereof and transdermal patch containing the composition

ABSTRACT

A Rotigotine-containing composition having a matrix mixture system formed from a polyvinylpyrrolidone and a combination of an acrylic pressure-sensitive adhesive with a silicone pressure-sensitive adhesive. The polyvinylpyrrolidone may be present in an amount of about 1-10% by weight in the matrix mixture system. The acrylic pressure-sensitive adhesive may be present in an amount of about 1-25% by weight in the matrix mixture system. The silicone pressure-sensitive adhesive may be present in an amount of about 65-98% by weight in the matrix mixture system. The composition further includes 1-40% of Rotigotine on the basis of the total weight of the composition. The composition provides improved properties in the solubility, release and initial penetration level of Rotigotine. Also disclosed is a transdermal patch that includes the Rotigotine-containing composition, as well as methods of manufacturing and using the Rotigotine-containing composition.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation application of U.S. patentapplication Ser. No. 12/667,915, filed Jun. 14, 2010, which isincorporated by reference herein in its entirety. U.S. application Ser.No. 12/667,915 entered the U.S. national stage from InternationalApplication No. PCT/CN2008/01267 filed Jul. 3, 2008. This applicationalso claims the benefit of Chinese Application No. 200710118491.X, filedJul. 6, 2007, and incorporated by reference herein in its entirety.

TECHNICAL FIELD

The present invention relates to a composition containing Rotigotine andthe use thereof in the manufacture of a Rotigotine-containingtransdermal patch, wherein said composition is based on a matrix mixturesystem formed from a combination of an acrylic pressure-sensitiveadhesive with a silicone pressure-sensitive adhesive, andpolyvinylpyrrolidone which are present in a particular weight ratio. Thepresent invention further relates to an improved transdermal patchcontaining Rotigotine comprising said composition. Said patch hasimproved properties in the solubility, release and initial penetrationlevel of Rotigotine.

Background Art

Rotigotine is a Non-Dihydroergotoxine D₃/D₂/D₁ dopamine receptoragonist, and long-term research shows that it has therapeutic effects ona variety of central nervous system diseases and mental disorders. Ascurrently known, Rotigotine has superior effects in regard to thetreatment or mitigation of Parkinson's disease, Restless Legs Syndrome,schizophrenia, depression and the like, and to the preventive treatmentof Parkinson's disease (WO2005/063237). In particular, the therapeuticand mitigative effects of Rotigotine on Parkinson's disease aresupported by substantive animal model studies and clinical tests(Neurology, Vol.65 Suppl1: S3-S5/movement disorders Vol. 9 No.2P147-154; ARCH NEUROL, Vol.60, December 2003: 1721-28). Rotigotine wasfirst formulated into oral formulations, but was then found to exhibitan overly high clearance and a relatively short duration of action afteroral intake. Thus, it could hardly achieve a therapeutically effectiveplasma concentration or be practically used owing to the need forfrequent drug administration (Neurology, Vol.65 Suppl1: S3-S5).Consequently, people tried to formulate Rotigotine into transdermalpatches.

WO99/49852 describes a transdermal drug delivery system comprisingRotigotine on the basis of an acrylate or silicone. The adhesive used inthis system is an acrylate or silicone, which independently of theother, forms a system involving a single adhesive together with theactive drug. The system comprising an acrylate as adhesive has a lowdrug release rate; the system comprising a silicone as adhesive has asmall drug load and a relatively low initial drug release rate.

WO2002/089778 describes the use of a silicone-based transdermaltherapeutic system in the manufacture of an anti-Parkinson's diseasemedicament. This transdermal therapeutic system comprises Rotigotine asactive ingredient. However, said system has a low drug release rate, andparticularly requires too long a period of time to achieve an effectivedosage. Consequently, there exist the following two problems: 1. thetransdermal patch has to be changed frequently, for example once per 24hours or shorter, to achieve an effective plasma concentration, and thisis contrary to the advantage of convenient use of the patch by apatient; 2. the transdermal patch has a relatively low initialpenetration level such that it takes too long a period of time for thedrug to take effect after the application of the patch, usuallyresulting in the delay of the control of a patient's state of illness.

The inventors have thoroughly investigated the inherent disadvantages ofthe existing Rotigotine transdermal delivery systems. After a lot oftests, the inventors have found out that a matrix mixture system formedfrom a combination of an acrylic pressure-sensitive adhesive with asilicone pressure-sensitive adhesive, and polyvinylpyrrolidone which arepresent in a particular weight ratio is capable of sufficientlydissolving and releasing an effective amount of Rotigotine and ofincreasing the initial penetration level of Rotigotine. Thus, theRotigotine releasing properties of the transdermal delivery system areimproved. The present invention is hence finished.

Contents of the Invention

The present invention provides a composition containing Rotigotine,which comprises, on the basis of the weight of the composition, 60-99%,preferably 70-95%, more preferably 75-90%, particularly preferably79-84% by weight, of a matrix mixture system and 1-40% by weight ofRotigotine, wherein the said matrix mixture system is formed from acombination of an acrylic pressure-sensitive adhesive with a siliconepressure-sensitive adhesive, and polyvinylpyrrolidone which are presentin a particular weight ratio, wherein:

-   -   (1) the acrylic pressure-sensitive adhesive is present in an        amount of about 1-25% by weight in the matrix mixture system,    -   (2) the silicone pressure-sensitive adhesive is present in an        amount of about 65-98% by weight in the matrix mixture system,        and    -   (3) the polyvinylpyrrolidone is present in an amount of about        1-10% by weight in the matrix mixture system.

In another aspect, the present invention provides the use of saidcomposition containing Rotigotine in the manufacture of a transdermalpatch.

Further still in another aspect, the present invention provides atransdermal patch containing Rotigotine, with a characteristic that thedrug-containing matrix layer of the patch is based on a matrix mixturesystem formed from a combination of an acrylic pressure-sensitiveadhesive with a silicone pressure-sensitive adhesive, andpolyvinylpyrrolidone which are present in a particular weight ratio,wherein:

-   -   (1) the acrylic pressure-sensitive adhesive is present in an        amount of about 1-25% by weight in the matrix mixture system,    -   (2) the silicone pressure-sensitive adhesive is present in an        amount of about 65-98% by weight in the matrix mixture system,        and    -   (3) the polyvinylpyrrolidone is present in an amount of about        1-10% by weight in the matrix mixture system, and        the drug-containing matrix layer comprises 1-40% of Rotigotine        on the basis of the total weight of the drug-containing matrix        layer.

In one embodiment, the Rotigotine-containing transdermal patch of thepresent invention has a multi-layer complex structure comprising abacking layer, a drug-containing matrix layer comprising the activeingredient Rotigotine and a covering layer on the drug-containing matrixlayer, with a characteristic that the drug-containing matrix layer isbased on a matrix mixture system formed from a combination of an acrylicpressure-sensitive adhesive with a silicone pressure-sensitive adhesive,and polyvinylpyrrolidone which are present in a particular weight ratio,wherein:

-   -   (1) the acrylic pressure-sensitive adhesive is present in an        amount of about 1-25% by weight in the matrix mixture system,    -   (2) the silicone pressure-sensitive adhesive is present in an        amount of about 65-98% by weight in the matrix mixture system,        and    -   (3) the polyvinylpyrrolidone is present in an amount of about        1-10% by weight in the matrix mixture system, and        the drug-containing matrix layer comprises 1-40% of Rotigotine        on the basis of the total weight of the drug-containing matrix        layer.

In the Rotigotine-containing composition of the present invention, theacrylic pressure-sensitive adhesive is present in an amount ofpreferably about 3-22%, more preferably about 4-20%, particularlypreferably about 5-19%, especially preferably about 6-12.5%, by weightin the matrix mixture system.

In the Rotigotine-containing composition of the present invention, thesilicone pressure-sensitive adhesive is present in an amount ofpreferably about 70-96%, more preferably about 75-95%, particularlypreferably about 79-94%, especially preferably about 86.5-93%, by weightin the matrix mixture system.

In the Rotigotine-containing composition of the present invention, thepolyvinylpyrrolidone is present in an amount of preferably about 1-8%,more preferably about 1-5%, particularly preferably about 1-2%,especially preferably about 1-1.5%, by weight in the matrix mixturesystem.

In the Rotigotine-containing composition of the present invention,Rotigotine is present in an amount of preferably about 3-20%, morepreferably about 5-15%, particularly preferably about 8-11%, on thebasis of the total weight of the composition.

The Rotigotine-containing composition of the present invention mayfurther optionally comprise auxiliaries commonly used in transdermaldrug delivery systems, such as permeation enhancers and antioxidants.

The Rotigotine-containing composition of the present inventionpreferably comprises a permeation enhancer, which may be present in anamount of about 0-15%, preferably about 2-13%, more preferably about5-11%, particularly preferably 8-10% on the basis of the total weight ofthe composition.

The Rotigotine-containing composition of the present invention maycomprise an antioxidant, which may be present in an amount of about0-0.1% on the basis of the total weight of the composition.

In a preferred embodiment of the composition according to the presentinvention, the composition comprises, on the basis of the total weightof the composition, about 70-95%, preferably about 75-90%, of the matrixmixture system, wherein the acrylic pressure-sensitive adhesive ispresent in an amount of about 3-22%, preferably about 4-20%, by weightin the matrix mixture system, the silicone pressure-sensitive adhesiveis present in an amount of about 70-96%, preferably about 75-95%, byweight in the matrix mixture system, and the polyvinylpyrrolidone ispresent in an amount of about 1-8%, preferably about 1-5%, by weight inthe matrix mixture system; and comprises, on the basis of the totalweight of the composition, about 3-20%, preferably about 5-15% by weightof Rotigotine and about 0-15%, preferably about 2-13% by weight of apermeation enhancer.

In a more preferred embodiment of the composition according to thepresent invention, the composition comprises, on the basis of the totalweight of the composition, about 75-90%, particularly about 79-84%, ofthe matrix mixture system, wherein the acrylic pressure-sensitiveadhesive is present in an amount of about 5-19%, particularly about6-12.5%, by weight in the matrix mixture system, the siliconepressure-sensitive adhesive is present in an amount of about 79-94%,particularly about 86.5-93%, by weight in the matrix mixture system, andthe polyvinylpyrrolidone is present in an amount of about 1-2%,particularly about 1-1.5%, by weight in the matrix mixture system; andcomprises, on the basis of the total weight of the composition, about5-15%, particularly about 8-11% of Rotigotine; and about 5-11%,particularly about 8-10% of a permeation enhancer.

The term “an acrylic pressure-sensitive adhesive” according to thepresent invention refers to an acrylic pressure-sensitive polymer andcombinations thereof with a Eudragit-type acrylic resin.

The term “an acrylic pressure-sensitive polymer” as used herein, refersto a type of polymers known in the art. Such a type of polymers isformed by copolymerization of acrylic acids and derivatives thereof, andhas a saturated hydrocarbon backbone and an ester side chain. A stickyacrylic pressure-sensitive polymer is obtainable by modifying theco-monomers and side chain groups. The monomers commonly used includesoft monomers such as ethyl acrylate, 2-ethylhexyl acrylate or isooctylacrylate, butyl acrylate and the like, for improving the adhesion of thepressure-sensitive polymers, hard monomers such as vinyl acetate, methylacrylate, styrene, acrylonitrile, C₁₋₁₀ alkyl methacrylate, e.g., methylmethacrylate, ethyl methacrylate and n-butyl methacrylate and the like,for improving the cohesion of the pressure-sensitive polymers, andfunctional monomers such as (meth)acrylic acid, (meth)acrylamide,β-hydroxyethyl (meth)acrylate, β-hydroxypropyl (meth)acrylate, glycidyl(meth)acrylate, N-hydoxylmethylacrylamide, divinylbenzene, maleic acid,maleic anhydride and the like (YANG Yukun, Pressure-Sensitive Adhesives,Science Press, June 1994, p.149-150), for forming chemical cross-links.The acrylic pressure-sensitive polymers used in the present inventionare those particularly preferably copolymerized from butyl acrylate,isooctyl acrylate, vinyl acetate, acrylamide and α-methacrylic acidmonomers. In particular, for example, the copolymer (A) of Example 2 inTable 1 on page 21 of CN1640500A (Beijing Kangbeide Pharmaceuticals Co.,Ltd), which is incorporated herein in its entirety by reference, i.e.PAS-10-K, is copolymerized from 33.1% of butyl acrylate, 40.9% ofisooctyl acrylate, 21.0% of vinyl acetate, 3.8% of acrylamide and 1.2%of α-methacrylic acid.

The term “a Eudragit-type acrylic resin”, as used herein refers to, butnot limited to, Eudragit® L100, Eudragit® S100, Eudragit® RL100,Eudragit® RS100, Eudragit® E100, Eudragit® L100-55, Eudragit® E PO,Eudragit® RL PO, Eudragit® RS PO and the like produced by Röhm Co. Ltd.(Germany), and Eudragit Nos. I, II, III and IV produced by JiangsuLianyun'gang Iodine Factory.

In the present invention, the acrylic pressure-sensitive adhesive ispreferably a mixture of an acrylic pressure-sensitive polymer with aEudragit-type acrylic resin, more preferably the acrylic-based adhesivecomposition disclosed in CN1640500A (Beijing Kangbeide PharmaceuticalsCo., Ltd), which consists of an acrylic pressure-sensitive polymer andEudragit® E100 (see the adhesive composition used in CN1640500A, page24, Table 4, Example 4), i.e. an adhesive composition consisting ofPAS-10-K and different percents of Eudragit® E100, and particularlypreferably an adhesive composition with a PAS-10-K to Eudragit® E100ratio of 9:1.

The silicone pressure-sensitive adhesives according to the presentinvention are a type of pressure-sensitive adhesives prepared bydissolving low-viscosity dimethyl silicone polymers (12,000 to 15,000cp) and silicone resins together in a suitable organic solvent. Theratio of resin to polymer and the silanol group content are importantparameters for the determination of the properties of the siliconepressure-sensitive adhesives (Sobieski, et al., “Silicone PressureSensitive Adhesives,” Handbook of Pressure Sensitive Technology, 2nded., 508-517, Van Nostrand Reinhold, New York (1989)). In the presentinvention, the silicone pressure-sensitive adhesives are preferablycommercially available, including the BIO-PSA® 4600 series, BIO-PSA®4500 series, BIO-PSA® 4400 series, BIO-PSA® 4300 series, BIO-PSA® 4200series and BIO-PSA® 4100 series silicone pressure-sensitive adhesivessold by Dow Corning Corporation. Anti-amine silicone pressure-sensitiveadhesives of the BIO-PSA° 4300 series and BIO-PSA® 4200 series are morepreferred.

The polyvinylpyrrolidone used in the present invention is useful as acrystallization inhibitor in transdermal drug delivery formulations.Polyvinylpyrrolidones or “PVPs” are non-ionic water-solublemacromolecular compounds formed by polymerization of N-vinylpyrrolidoneunder certain conditions. The use of polyvinylpyrrolidones intransdermal drug delivery formulations is already mentioned inEP0524776. Suitable PVPs include the products under the trademarkKollidon produced by BASF. In the present invention, Kollidon 17PF, 25,30 and 90 are preferably used, and Kollidon 30 and Kollidon 90 areparticularly preferred.

The inventors have found out, after conducting a lot of tests, that amatrix mixture system comprising a combination of an acrylicpressure-sensitive adhesive with a silicone pressure-sensitive adhesivein a certain ratio improves the solubility and skin permeability of thedrug significantly, and the addition of a small amount ofpolyvinylpyrrolidone further improves the drug load and penetrationlevel without affecting the mechanical properties of the patch. Althoughan increased percent by weight of the acrylic pressure-sensitiveadhesive in the matrix mixture system increases the solubility andinitial dispersion rate of the drug, it lowers the drug's sustainedrelease ability in the system, and finally results in a relatively highlevel of drug residue after the application of the patch. A decreasedpercent by weight of the acrylic pressure-sensitive adhesive in thematrix mixture system fails to increase the initial dispersion rate ofthe drug. Thus, the ratio of the acrylic pressure-sensitive adhesive tothe silicone pressure-sensitive adhesive is within a limited range. Thepolyvinylpyrrolidone is a solubility enhancer and crystallizationinhibitor. Anyone with ordinary skill in the art can determine itssuitable amount by conducting conventional tests. In the system, anexcessively high polyvinylpyrrolidone content will affect the mechanicalproperties of the patch, and a suitable amount of polyvinylpyrrolidonecan change the dispersion state of the drug in the system.

In the transdermal patch containing Rotigotine of the present invention,the acrylic pressure-sensitive adhesive is present in an amount of about1-25%, preferably about 3-22%, more preferably about 4-20%, particularlypreferably about 5-19%, especially preferably about 6-12.5%, by weightin the matrix mixture system.

In the transdermal patch containing Rotigotine of the present invention,the silicone pressure-sensitive adhesive is present in an amount ofabout 65-98%, preferably about 70-96%, more preferably about 75-95%,particularly preferably about 79-94%, especially preferably about86.5-93%, by weight in the matrix mixture system.

In the transdermal patch containing Rotigotine of the present invention,the polyvinylpyrrolidone is present in an amount of about 1-10%,preferably about 1-8%, more preferably about 1-5%, particularlypreferably about 1-2%, especially preferably about 1-1.5%, by weight inthe matrix mixture system.

In the transdermal patch containing Rotigotine of the present invention,the Rotigotine is present in an amount of about 1-40%, preferably about3-20%, more preferably about 5-15%, particularly preferably about 8-11%,on the basis of the total weight of the drug-containing matrix layer.

In the transdermal patch containing Rotigotine of the present invention,the matrix mixture system is present in an amount of 60-99%, preferably70-95%, more preferably 75-90%, particularly preferably 79-84%, on thebasis of the total weight of the drug-containing matrix layer.

In the transdermal patch of the present invention, the drug-containingmatrix layer may optionally comprise auxiliaries commonly used intransdermal drug delivery systems, such as permeation enhancers,antioxidants and so on, so as to assist to improve the properties of thepatch.

The transdermal patch of the present invention preferably comprises apermeation enhancer, which may be present in an amount of about 0-15%,preferably about 2-13%, more preferably about 5-11%, particularlypreferably 8-10% on the basis of the total weight of the drug-containingmatrix layer.

The transdermal patch of the present invention may comprise anantioxidant, which may be present in an amount of about 0-0.1% on thebasis of the total weight of the drug-containing matrix layer.

In a preferred embodiment of the transdermal patch according to thepresent invention, the drug-containing matrix layer of the transdermalpatch comprises, on the basis of the total weight of the drug-containingmatrix layer, about 70-95%, preferably about 75-90%, of the matrixmixture system, wherein the acrylic pressure-sensitive adhesive ispresent in an amount of about 3-22%, preferably about 4-20%, by weightin the matrix mixture system, the silicone pressure-sensitive adhesiveis present in an amount of about 70-96%, preferably about 75-95%, byweight in the matrix mixture system, and the polyvinylpyrrolidone ispresent in an amount of about 1-8%, preferably about 1-5%, by weight inthe matrix mixture system; and comprises, on the basis of the totalweight of the drug-containing matrix layer, about 3-20%, preferablyabout 5-15% of Rotigotine; and about 0-15%, preferably about 2-13% of apermeation enhancer.

In a more preferred embodiment of the transdermal patch according to thepresent invention, the drug-containing matrix layer of the transdermalpatch comprises, on the basis of the total weight of the drug-containingmatrix layer, about 75-90%, particularly about 79-84%, of the matrixmixture system, wherein the acrylic pressure-sensitive adhesive ispresent in an amount of about 5-19%, particularly about 6-12.5%, byweight in the matrix mixture system, the silicone pressure-sensitiveadhesive is present in an amount of about 79-94%, particularly about86.5-93%, by weight in the matrix mixture system, and thepolyvinylpyrrolidone is present in an amount of about 1-2%, particularlyabout 1-1.5%, by weight in the matrix mixture system; and comprises, onthe basis of the total weight of the drug-containing matrix layer, about5-15%, particularly about 8-11% of Rotigotine; and about 5-11%,particularly about 8-10% of a permeation enhancer.

Permeation enhancers useful in the present invention may be selectedfrom the group consisting of (1) surfactants, such as tweens, spans,sodium lauryl sulfate, sodium dodecylsulfate and the like, (2) organicsolvents including alcohols, polyols, esters, dimethyl sulfoxide andanalogues thereof, specific examples may be mentioned, such as ethylacetate, propylene glycol diacetate, glycol, glycerine, dimethylsulfoxide, decylmethyl sulfoxide etc., (3) fatty acids, fatty alcoholsand fatty acid esters, such as oleic acid, lactic acid, myristic acid,lauryl acid, isopropyl myristate and the like, (4) azones andpyrrolidone derivatives, such as N-methylpyrrolidone,1,5-dimethylpyrrolidone, 5-carboxylpyrrolidone and the like, (5)keratinous emollients and softeners, such as salicylic acid and urea,and (6) terpenes, such as menthol, camphor and the like. Isopropylmyristate, lauryl acid and N-methylpyrrolidone are preferred.

A variety of antioxidants are suitable for use in the present invention.For example, suitable antioxidants may be selected from inorganic andorganic antioxidants and determined by conventional stability tests inthe art. Said antioxidants may be selected from, for example, the groupconsisting of vitamin E, ascorbyl palmitate, sodium metasulfite ormixtures thereof. Vitamin E and ascorbyl palmitate are preferred.

The active ingredient, Rotigotine used in the present invention may be afree base of Rotigotine or a pharmaceutically acceptable salt ofRotigotine, such as a hydrochloride, sulfate, nitrate or succinate ofRotigotine, but a free base of Rotigotine is preferred.

In the transdermal patch of the present invention, the backing layer ismade from a backing material well known by those with skill in the art;such a backing material may be aluminum foil, polyethylene glycolterephthalate, polyethylene or non-woven fabric. In the transdermalpatch of the present invention, the covering layer applied on thedrug-containing matrix layer is made from a protective material wellknown by those with skill in the art; such a protective material may bea polyester, polyvinyl chloride or polyethylene glycol terephthalatefilm, or the above-mentioned film is treated conventionally with arelease coating, including the application of a silicone resin orfluorine resin on the surface of the film in direct contact with thedrug-containing matrix layer. The covering layer of the transdermalpatch of the present invention is preferably the polyester film surfacecoated with a fluorine resin.

The transdermal patch of the present invention may be processed intovarious shapes and sizes in regard to practical needs, and its surfacearea is preferably 1.0-150 cm² with preferred specifications of 4.5 mgRotigotine/10 cm², 9 mg Rotigotine/20 cm², 13.5 mg Rotigotine/30 cm²,and 18 mg Rotigotine/40 cm².

The drug-containing matrix layer of the Rotigotine-containingtransdermal patch of the present invention has a thickness of 20-80 μm,preferably 40-60 μm.

The drug-containing matrix layer of the Rotigotine-containingtransdermal patch of the present invention may be in the form of amono-layer or multi-layer complex well-known in the art. Suchtransdermal patch structure may comprise a backing layer, a high-contentactive drug Rotigotine layer and/or an intermediate-content active drugRotigotine layer, a low-content active drug Rotigotine layer, and acovering layer.

The Rotigotine-containing composition of the present invention can beprepared by techniques known in the art. For example, in accordance withthe formula, polyvinylpyrrolidone is weighed into a suitable container,a suitable amount of the solution of an antioxidant (if present) inethanol is added, and the polyvinylpyrrolidone is dissolved by stirring.Into the same container, Rotigotine, a silicone pressure-sensitiveadhesive, an acrylic pressure-sensitive adhesive (wherein the acrylicpressure-sensitive polymer is prepared according to the process forpreparing a (meth)acrylate copolymer comprising (meth)acrylamide or anN,N-substituted monomer thereof as described in the Example on pages20-21 of CN1640500A) and an optional permeation enhancer are addedaccording to the formula, a suitable amount of a solvent, such as ethylacetate, is added, and the components are sufficiently dissolved bystirring. At last, the polyvinylpyrrolidone is completely dissolved byadding a suitable amount of ethanol and performing ultrasonic treatmentfor 30 minutes, and a Rotigotine-containing composition is thusprepared.

The transdermal patch of the present invention may be prepared bytechniques known in the art. The techniques comprise for example, thefollowing steps:

1. Adding into a suitable container, polyvinylpyrrolidone according tothe formula, a suitable amount of a solution of an antioxidant (ifpresent) in ethanol and stirring to dissolve the polyvinylpyrrolidone;

2. Adding into the same container, Rotigotine, a siliconepressure-sensitive adhesive, an acrylic pressure-sensitive adhesive(wherein the acrylic pressure-sensitive polymer is prepared according tothe process for preparing a (meth)acrylate copolymer comprising(meth)acrylamide or an N,N-substituted monomer thereof as described inthe Example on pages 20-21 of CN1640500A) and an optional permeationenhancer according to the formula, a suitable amount of a solvent suchas ethyl acetate to build up the volume to a certain level, and stirringto sufficiently dissolve the components;

3. Adding a suitable amount of ethanol and performing ultrasonictreatment for 30 minutes to completely dissolve thepolyvinylpyrrolidone, at which point the resultant mixture becomes clearand transparent, hence obtaining the material for the drug-containingmatrix layer of the transdermal patch;

4. Finally, applying the resulting material with a certain thickness ona patulous backing material, primarily drying it by air, then moving itto an oven where it is dried for 2 hours at 80° C., removing thevolatile solvent prior to taking it out and cooling it, later applyingit with a covering layer, and finally die-cutting it to patches withcertain surface areas and shapes.

The transdermal patch of the present invention comprising adrug-containing matrix layer in the form of a multi-layer complex may beprepared according to a conventional process known in the art. Forexample, first of all, matrices comprising the same concentration ordifferent concentrations of the active drug are formulated. Then thematrices are respectively applied to a backing support material and aspecially made, protective liner by a scraper method and dried to takeshape. Subsequently, the matrix layer applied on the protective liner istransferred onto the matrix layer applied on the backing supportmaterial, the protective liner is removed, the layers are transferredone by one according to this method and laminated, then a covering layeris applied onto the laminate, and finally patches comprising adrug-containing matrix layer in the form of multi-layer complex aredie-cut into certain surface areas and shapes (see LIANG Bingwen,Transdermal Drug Delivery Formulations, China Medical-PharmaceuticalScience and Technology Publishing House, September 1992, p.329-334).

The present invention provides a transdermal patch containing Rotigotinewhich can sufficiently dissolve and release an effective amount of drug,Rotigotine. This patch has an increased Rotigotine initial penetrationlevel. Judging from this feature, it can be predicted that thetransdermal patch containing Rotigotine of the present invention needs arelatively short period of time to take effect in clinical use.

DESCRIPTION OF THE DRAWING

FIG. 1 shows the curve of the in vitro transdermal release amount(μg/cm²) accumulated from 1 to 72 hours of Rotigotine in the transdermalpatches of Example 1 (the present invention), NEUPRO® (ComparativeExample 1) and Comparative Examples 2-5.

EXAMPLES

The present invention is further illustrated by, but not limited to, thefollowing Examples.

Preparation of a Transdermal Patch

Example 1

Into a suitable container, 0.05 g of polyvinylpyrrolidone (Kollidon 30produced by BASF Germany) was added, 1 ml of a solution of ascorbylpalmitate (produced by Beijing Chen Ao Hi-Tech Co. Ltd.) in ethanol (3mg/ml) as antioxidant was added, and the polyvinylpyrrolidone wasdissolved by stirring. Into the same container, 0.45 g of a Rotigotinebase (which was synthesized and prepared according to the processdescribed in “Synthesis and radioreceptor binding activity of N-0437, anew, extremely potent and selective D2 dopamine receptor agonist”, PharmWeekbl Sci, Vol.7.1985:208-211), 6.25 g of a 30% solid content siliconepressure-sensitive adhesive (BIO-PSA® 7-4302 Dow Corning Corporation),0.72 g of a 35% solid content acrylic pressure-sensitive adhesive (whichwas prepared according to the process for preparing a (meth)acrylatecopolymer comprising (meth)acrylamide or an N,N-substituted monomerthereof as described in the Example on pages 20-21 of CN1640500A,wherein the monomer used in Example 2 was used for the preparation of anacrylic pressure-sensitive polymer, and the acrylic pressure-sensitivepolymer thus prepared was mixed with Eudragit® E100 (produced by RohmGermany) in a ratio of 9:1 (dry weight)) and 0.5 g of isopropylmyristate (Jiangsu Kunshan Huaxin Daily Chemicals Co., Ltd) was added. Asuitable amount of ethyl acetate (produced by Beijing Organic ChemicalPlant, chemically pure) was added to build up the volume to a certainlevel, and the components were sufficiently mixed by stirring.Subsequently, a suitable amount of ethanol (produced by Beijing YiliFine Chemical Co., Ltd., chemically pure) was added, and ultrasonictreatment was performed for 30 minutes to completely dissolve thepolyvinylpyrrolidone to form a mucilage. At that time, the mucilage wasclear and transparent. The resulting mucilage was applied with a certainthickness to a backing material of a patulous polyester film (SCOTCHPAK®1109) to prepare a drug-containing matrix layer, and then dried at 85°C. for 2 to 3 hours to obtain a thickness of about 40 pm. Afluorine-containing layer-coated polyester film (SCOTCHPAK® 1022) wasthen applied on the resulting drug-containing matrix layer, and finallythe resultant layers were die-cut to produce patches having certainsurface areas and sizes, i.e. the transdermal patches of the presentinvention. The patches contained 0.45 mg/cm² of Rotigotine and theamounts (parts by weight) of the other components as shown in Table 1.

Examples 2 to 3

Patches of Examples 2 and 3 were prepared according to the processdescribed in Example 1 wherein the components of the drug-containingmatrix layer and the amounts thereof (parts by weight) were as shown inTable 1.

Examples 4 to 8

Patches of Examples 4-8 were prepared according to the process describedin Example 1, wherein the components of the drug-containing matrix layerand the amounts thereof (parts by weight) were as shown in Table 2.

Comparative Example 1

A commercially available Rotigotine patch NEUPRO® was obtained fromSchwarz Pharm AG. with a Rotigotine content of 0.45 mg/cm²

Comparative Examples 2 to 5

Patches prepared according to the process described in Example 1: theformula of Comparative Example 2 contained no siliconepressure-sensitive adhesives, the formula of Comparative Example 3contained no acrylic pressure-sensitive adhesive, the formula ofComparative Example 4 contained no polyvinylpyrrolidone (the process forthe preparation of the patch of Comparative Example 4 did not have thestep of dissolving polyvinylpyrrolidone), and the amounts of the acrylicand silicone pressure-sensitive adhesives in the formula of ComparativeExample 5 were beyond the ranges of the present invention. The specificformulae of the drug-containing matrix layers of these patches are asshown in Table 1.

Measurement of the Release amount of Rotigotine in the TransdermalPatches

The above-mentioned patches were subjected to in vitro transdermal testsaccording to the experimental methods introduced by the Transdermal DrugDelivery Formulations (LIANG Bingwen, China Medical—PharmaceuticalScience and Technology Publishing House, September 1992, p.252).

Experimental Apparatus: FRANZ-type transdermal diffuser (Model: TK-60B,Shanghai Kaikai Technology&Trade Co., Ltd.)

Experimental Carrier: freshly prepared whole-thickness skin from the ribpart and back of a guinea pig (prepared according to the TransdermalDrug Delivery Formulations, LIANG Bingwen, China Medical—PharmaceuticalScience and Technology Publishing House, September 1992, p.252)

Number of Samples: 5 (five samples for each tested subject of thepatches of the Examples or Comparative Examples)

Patch Surface Area: 10 cm²

Diffusion Medium: a phosphate buffer of pH 6.2

Measuring Method: high-performance liquid chromatography (UV detector,Waters, Model: 2487)

The 1-72 hours accumulative release amounts (μg/cm²) of Rotigotine inthe patches of Example 1 and Comparative Examples 1-5 were measured, andthe results are as shown in FIG. 1. The 0-12 hours accumulative releaseamounts (μg/cm²) of Rotigotine in the patches of Examples 1-3 andComparative Examples 2-5 are as shown in Table 1.

TABLE 1 Example Example Example Comparative Comparative ComparativeComparative Drug-containing 1 2 3 Example 2 Example 3 Example 4 Example5 matrix layer Parts by weight Acrylic pressure- 5 10 15 80 — 5 50sensitive adhesive Silicone pressure- 75 70 65 — 80 75 30 sensitiveadhesive (BIO-PSA ® 7-4302) Polyvinylpyrrolidone 1 1 1 1 1 — 1 (Kollidon30) Rotigotine base 9 9 9 9 9 9 9 Isopropyl myristate 10 10 10 10 10 1110 Ascorbyl palmitate 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.00060-12 hours accumulative 226.7 221.4 210.3 86.3 181.4 117.7 144.7 releaseamounts (μg/cm²) of Rotigotine

Note: All the Examples and Comparative Examples (including the testsample of NEUPRO® of Comparative Example 1) contain the same amount ofRotigotine (0.45 mg/cm²) to ensure the comparability of the experimentalresults.

TABLE 2 Drug-containing Example 4 Example 5 Example 6 Example 7 Example8 Matrix layer Parts by weight Acrylic pressure- 5 5 5 5 5 sensitiveadhesive Silicone pressure- 93 84 70 65 65 sensitive adhesive (BIO-PSA ®7-4302) Polyvinylpyrrolidone 1 1 2 2 2 (Kollidon 30) Rotigotine base 1 515 18 25 Isopropyl myristate 0 5 8 10 3 Ascorbyl palmitate 0.0006 0.00060.0006 0.0006 0.0006

It can be seen from FIG. 1 that Example 1 of the present invention had ahigher transdermal release amount than NEUPRO® and the patches of theother Comparative Examples, and showed the characteristic of zero-orderrelease. More importantly, it can be seen from FIG. 1 that thetransdermal patches of the present invention had a significantlyincreased drug penetration level within the initial 12 hours ofdiffusion, which means that the patches took effect faster. It can beseen from FIG. 1 and Table 1 that the transdermal patches of the presentinvention exhibited unique advantages of Rotigotine transdermal rateover the patches of Comparative Examples 2-5, and had the properties ofa longer duration and a uniform drug release.

1. A rotigotine-containing transdermal patch comprising a matrix layercomposition, wherein the matrix layer composition comprises, on thebasis of the total weight of the matrix layer composition, 60-99% byweight of a matrix mixture system and 1-40% by weight of rotigotine,wherein the matrix mixture system is formed from a combination of anacrylic pressure-sensitive adhesive with a silicone pressure-sensitiveadhesive, and polyvinylpyrrolidone, wherein (1) the acrylicpressure-sensitive adhesive is present in an amount of 5-19% by weightin the matrix mixture system, (2) the silicone pressure-sensitiveadhesive is present in an amount of 79-94% by weight in the matrixmixture system, and (3) the polyvinylpyrrolidone is present in an amountof 1-10% by weight in the matrix mixture system; and wherein therotigotine is in the form of free base or a pharmaceutically acceptablesalt.
 2. The rotigotine-containing transdermal patch of claim 1, whereinthe matrix layer composition further comprises at least one auxiliaryselected from the group consisting of permeation enhancers andantioxidants.
 3. The rotigotine-containing transdermal patch of claim 2,wherein the permeation enhancer is selected from the group consisting ofsurfactants, organic solvents including alcohols, polyols, esters,dimethyl sulfoxide, fatty acids, fatty alcohols, fatty acid esters,azones, pyrrolidone derivatives selected from the group consisting ofN-methylpyrrolidone, 1,5-dimethylpyrrolidone and 5-carboxylpyrrolidone,salicylic acid and terpenes.
 4. The rotigotine-containing transdermalpatch of claim 2, wherein the antioxidant is selected from the groupconsisting of vitamin E, ascorbyl palmitate, sodium metasulfite andmixtures thereof.
 5. The rotigotine-containing transdermal patch ofclaim 1, wherein the acrylic pressure-sensitive adhesive is selectedfrom the group consisting of an acrylic pressure-sensitive polymer and acombination of an acrylic pressure sensitive polymer with an acrylicresin.
 6. The rotigotine-containing transdermal patch of claim 5,wherein the acrylic pressure-sensitive polymer is copolymerized from asoft monomer, a hard monomer and a functional monomer, wherein the softmonomer is selected from the group consisting of ethyl acrylate,2-ethylhexyl acrylate, isooctyl acrylate, and butyl acrylate, the hardmonomer is selected from the group consisting of vinyl acetate, methylacrylate, styrene, acrylonitrile, methyl methacrylate, ethylmethacrylate, and n-butyl methacrylate, and the functional monomer isselected from the group consisting of (meth)acrylic acid,(meth)acrylamide, β-hydroxyethyl (meth)acrylate, β-hydroxypropyl(meth)acrylate, glycidyl (meth)acrylate and N-hydoxylmethylacrylamide.7. The rotigotine-containing transdermal patch of claim 6, wherein theacrylic pressure-sensitive polymer is copolymerized from the monomers:butyl acrylate, isooctyl acrylate, vinyl acetate, acrylamide andα-methacrylic acid.
 8. The rotigotine-containing transdermal patch ofclaim 2, wherein the matrix layer composition comprises, on the basis ofthe total weight of the matrix layer composition, 75-90% by weight ofthe matrix mixture system, 5-15% by weight of rotigotine and 5-11% byweight of the permeation enhancer.
 9. The rotigotine-containingtransdermal patch of claim 8, wherein the matrix layer compositioncomprises, on the basis of the total weight of the matrix layercomposition, 79-84% by weight of a matrix mixture system, 8-11% byweight of rotigotine and 8-10% by weight of the permeation enhancer,wherein the acrylic pressure-sensitive adhesive is present in an amountof 6-12.5% by weight in the matrix mixture system, the siliconepressure-sensitive adhesive is present in an amount of 86.5-93% byweight in the matrix mixture system, and the polyvinylpyrrolidone ispresent in an amount of 1-1.5% by weight in the matrix mixture system.10. The rotigotine-containing transdermal patch of claim 8, wherein thepermeation enhancer is selected from the group consisting of isopropylmyristate, lauryl acid and N-methylpyrrolidone.
 11. Therotigotine-containing transdermal patch of claim 1, wherein thepolyvinylpyrrolidone is present in an amount of 1-2% by weight in thematrix mixture system.